Bump-on-Trace Interconnect

ABSTRACT

Disclosed herein is a bump-on-trace interconnect with a wetted trace sidewall and a method for fabricating the same. A first substrate having conductive bump with solder applied is mounted to a second substrate with a trace disposed thereon by reflowing the solder on the bump so that the solder wets at least one sidewall of the trace, with the solder optionally wetting between at least half and all of the height of the trace sidewall. A plurality of traces and bumps may also be disposed on the first substrate and second substrate with a bump pitch of less than about 100 μm, and volume of solder for application to the bump calculated based on at least one of a joint gap distance, desired solder joint width, predetermined solder joint separation, bump geometry, trace geometry, minimum trace sidewall wetting region height and trace separation distance.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is related to, and claims priority to U.S. Provisional Application No. 61/625,980, titled, “Semiconductor Device Package” filed on Apr. 18, 2012, which is herein incorporated by reference.

BACKGROUND

Generally, one of the driving factors in the design of modern electronics is the amount of computing power and storage that can be shoehorned into a given space. The well-known Moore's law states that the number of transistors on a given device will roughly double every eighteen months. In order to compress more processing power into ever smaller packages, transistor sizes have been reduced to the point where the ability to further shrink transistor sizes has been limited by the physical properties of the materials and processes. Designers have attempted to overcome the limits of transistor size by packaging ever larger subsystems into one chip (systems on chip), or by reducing the distance between ships, and subsequent interconnect distance.

One method used to reduce the distance between various chips forming a system is to stack chips, with electrical interconnects running vertically. This can involve multiple substrate layers, with chips on the upper and lower surfaces of a substrate. One method for applying chips to the upper and lower side of a substrate is called “flip-chip” packaging, where a substrate has conductive vias disposed through the substrate to provide an electrical connection between the upper and lower surfaces.

Solder ball grid arrays are also a technique sometimes used to joining packages, with an array of solder balls deposited on the bonding pads of a first package, and with a second package joined at its own bonding pad sites to the first pad via the solder balls. The environment with the solder ball grid array is heated to melt the solder balls and the packages compressed to cause the solder balls to contact the pads on both packages.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present disclosure, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawing, in which:

FIGS. 1 and 2 are cross-sectional diagrams of embodiments of a BoT interconnect element;

FIG. 3 is an enlarged cross-sectional illustration of a BoT interconnect;

FIG. 4 is cross-sectional illustration of multiple BoT interconnects; and

FIGS. 5A-5D are illustrations of embodiments of BoT interconnects.

DETAILED DESCRIPTION

The making and using of the presented embodiments are discussed in detail below. It should be appreciated, however, that the present disclosure provides many applicable concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the described package, and do not limit the scope of the disclosure.

Embodiments will be described with respect to a specific context, namely making and using bump-on-trace interconnects useful in, for example, package-on-package assemblies. Other embodiments may also be applied, however, to other electrically connected components, including, but not limited to, bare chips, displays, input components, board mounting, die or component mounting, or connection packaging or mounting of combinations of any type of integrated circuit or electrical component.

The embodiments of the present disclosure are described with reference to FIGS. 1 through 5D, and variations of the embodiments are also discussed. Throughout the various views and illustrative embodiments of the present disclosure, like reference numbers are used to designate like elements. Additionally, the drawings are intended to be illustrative, are not to scale and not intended to be limiting. Note that, for simplification, not all element numbers are included in each subsequent drawing. Rather, the element numbers most pertinent to the description of each drawing are included in each of the drawings.

The present concepts are directed to providing a system and method for creating interconnections having a solder based bump-on-trace (BoT) connection with an improved pitch. Additionally, the disclosed embodiments are not limited to bump-on-trace applications, but may be applied to lead grid arrays (LGAs) where an array of conductive structures protrudes from a package for attachment to another package. LGA leads may be formed to have flexibility to absorb thermal or physical stress in a package-on-package connection, and solder may be applied to a portion of each LGA lead to attach the lead to a trace or bump.

With BoT connectors having fine pitches (<100 μm), the bump solder tends to not wet the sidewall of a trace under a thermal compression bonding/nonconductive paste (TCB/NCP) process, negatively impacting joint integrity and electro-migration performance. BoT interconnect systems may provide a higher density of interconnects than alternative methods of packaging, and reduce the failure rate of interconnected assemblies. BoT interconnects may be used to attach, or stack multiple packages vertically, connecting the stacked packaged via redirection layer (RDL) contacts, electrical traces, mounting pads or the like.

In general terms, in the illustrated embodiments, a BOT joint can achieve fine pitch assembly with significant trace sidewall solder wetting. In one embodiment, one or both of the trace sidewalls may be wetted, or covered, by solder, at more than half the trace height. Sidewall wetting may provide for advantageous features that include, but are not limited to, improved joint integrity (e.g., reduced trace peeling and T0 joint cracking) and improved electro-migration (EM) performance.

Referring to FIG. 1, a cross-sectional diagram of an embodiment of a package 100 with a sidewall wetting BoT interconnect is depicted. A pillar or bump 122 may be disposed on a first substrate 102 or on another package. In one embodiment, the bump 122 may be copper (Cu), or it may be gold (Au), silver (Ag), palladium (Pd), tantalum (Ta), tin (Sn), lead (Pb), alloys of the same, or another conductive material. Additionally, the bump 122 may have an adhesion or anticorrosion coating such as an organic solderability preservative (OSP), tin (Sn), nickel-gold alloy (NiAu), nickel-platinum-gold alloy (NiPtAi) or the like. While the top package is herein referred to as a first substrate 102, in other embodiments, a flip chip, a display, package, PCB, input board, or any other electronic device may be used within the scope of the present disclosure. Additionally, while a single level of interconnects are described herein, the present disclosure may be applied to a system having multiple packages on any number of levels or in any arrangement. For example, a memory chip may be mounted on a processor using a sidewall wetting BoT interconnect, and the processor/memory combination may be mounted to a PCB or other target package using the sidewall wetting BoT interconnect technique disclosed herein.

In one embodiment, a first substrate 102 may be a chip, package, PCB, die, or the like, and may have a die substrate 104 and one or more metallization layers 106. The metallization layer 106 may, in one embodiment, include a conductive land 108, metallic traces, vias, or the like. An oxide or insulating layer 110 and passivation layer 112 may each optionally be disposed on the surface of the first substrate 102, and may define an opening over the conductive land 108 for the bump 122 to contact or attach to the conductive land 108. In such an embodiment, the bump 122 may be disposed covering a portion of, or the entire exposed portion of, the conductive land 108 not covered by the insulating layer 110 and passivation layer 112. Additionally, the bump 122 may be disposed to cover or contact a portion of the insulation layer 110 or passivation layer 112. In such an embodiment, the bump 122 may be disposed over the conductive land 108 and the insulating layer 110 or passivation layer 112. In some embodiments, the bump 122 may completely cover the conductive land 108 and contact the insulating layer 110 or passivation layer 112 on all sides of the conductive land 108 to seal the conductive land 108 from the environment.

The first substrate 102 may be electrically coupled to a die substrate 114 disposed in the second substrate 120 and having a conductive trace 116 formed thereon. The trace 116, in one embodiment, may be deposited as a blanket surface and patterned, but in other embodiments, may be formed via a damascene process, or the like. Additionally, the trace 116 may, in one embodiment, be copper, or another conductive material, and may optionally have an anticorrosion coating such as an OSP, metallic coating or the like.

Application of a conductive material 124, such as solder, may assist in retaining the electrical connection between the bump 122 and the trace 116. Solder joints avoid electromigration issues, and the use of sidewall wetting creates a stronger joint at the solder joint 124 to trace 116 junction. Such sidewall wetting may prevent cracking of the joint, or delamination of the solder joint 124 from the trace 116, die in part to an increased surface area, but also due to the material wetting the trace 116 sidewall preventing lateral movement of the solder with respect to the trace 116.

Thermal compression bonding is the welding of two metallic structures using heat and pressure. However, imperfections, such a surface irregularities, oxidation or contaminants on the mating surfaces may create voids when two surfaces are brought together for bonding. Electromigration exists where the flow of electrons in a metal causes atoms to move due to the electrons striking the atom and transferring the electrons' momentum to the atom. EM is a particular problem in small PCB joints due to the grain boundary of the like metals forming the joints, as the migration of metal atoms tends to occur around any voids or impurities in the interface between the two structures forming the joint. This atom migration amplifies the imperfections in the joint, eventually leading to physical failure of the joint.

In one embodiment a conductive material is used to form a mechanical and electrical connection between the bump 122 and trace 116. In some embodiments, the conductive material may be solder; however, another fusible conductive material may be used, such as, but not limited to gold, conductive adhesive, solder paste, or the like. The illustrated configuration illustrates one embodiment with wetting of the sidewalls of the trace 116, which will preferably be at least half the height of the trace 116 sidewall. In another embodiment, the sidewalls of the trace 116 will have solder disposed on, or wetting, at least a portion of one trace 116 sidewall. The wetting may be promoted by treating the trace 116 sidewall to more readily accept the solder. In some embodiments, an active plasma treatment may be applied to prepare the surface for application of the solder joint 124. In another embodiment, the trace 116 sidewall may be chemically treated, for example, to remove oxidation or foreign material from the surface of the trace. However, wetting may be promoted by any process, including surface etching, applying a flux, applying a solder preservative, or the like.

Additionally, the region of the trace 116 sidewall wetted by the solder joint 124 will be a contiguous portion of the solder joint 124, with the entirety of the solder joint 124 being applied or formed in a single step. For example, the solder joint 124 may be reflowed and solidified to create a uniform structure over the trace 116. In another embodiment, the solder joint 124 may extend past the face, or surface of the bump 122 opposite the first substrate 102, and may cover a portion of a sidewall of the bump 122.

The embodiment illustrated in FIG. 1 shows bump 122 having substantially vertical sidewalls. Skilled artisans will recognize that the bump 122 may have a sidewall slope that varies depending on the requirements of the joint. For example, the bump 122 may have sloped sides, or may have a curved or partially circular vertical cross section. Additionally, while the foregoing examples are described in terms of the vertical cross-section, the bump 122 may have virtually any advantageous horizontal cross section. For example, the bump 122 may have a round, square, rectangular or irregularly shaped base in combination with any vertical cross section.

FIG. 2 depicts a cross-sectional diagram of an alternative embodiment of a package 200 with a sidewall wetting BoT interconnect. In such an embodiment, the sidewalls of the bump 122 may be sloped, with the broader, or wider, portion of the bump 122 being disposed at the first substrate 102, and the narrower end having the solder joint 124 disposed thereon. The wider end of the bump may be disposed on the first substrate 102 conductive land 108 and covering a portion of the insulating layer 110 and passivation layer 112. In such an embodiment, the trace 116 may have a portion of the solder joint 124 wetting, or disposed on, a portion of the sidewalls.

FIG. 3 is an enlarged cross-sectional illustration 300 of a BoT interconnect. Use of a wetted sidewall trace BoT joint may also permit a finer pitch between adjacent interconnects structures. FIG. 4 is cross-sectional illustration of multiple BoT interconnects. In the embodiments shown in FIGS. 3 and 4, the bump 122 has sloped sidewalls, however, a parallel or straight sided bump 122, as illustrated in FIG. 1, or any other described or useful bump shape may be used as well.

Referring now to FIG. 3, the bump face 310 may have a bump face width 312 that may be wider than the trace width 314. The solder joint 124 may have a width greater than the trace width 314. The portion of the solder joint 124 exceeding the trace width 314 may extend below the face of the trace to wet the sidewall of the trace 116. Additionally, in some embodiments, the width of the solder joint 124 may exceed the bump face width 312 to wet the sidewalls of the bump 122. In another embodiment, the width of the solder joint 124 may be about equal to the bump face width 312 and wet the sidewalls of the trace 116. In yet another embodiment, the bump face 310 may be disposed above and separate from the trace 116 by a predetermined joint gap distance 308 that is sufficient to permit solder to reflow through the gap without voids and result in a predetermined joint height.

The sidewall height 302 is comprised of the sidewall wetted region height 304 and the sidewall unwetted region height 306. In one embodiment, the sidewall wetted region height 304 may be at least half of the sidewall height 302. In another embodiment, the sidewall wetted region height 304 may be equal to the sidewall height 302, that is, the entire trace 116 sidewall may be wetted by the solder joint 124.

In one embodiment, the joint gap distance 308 may be the same as the height of the trace, or sidewall height 302. In another embodiment, the joint gap distance 308 may be less than the sidewall height 302 of the trace 116. Therefore, the joint gap distance 308 may be sufficient to permit solder to flow into the gap, and less than the sidewall height 302 of the trace 116.

Referring now to FIG. 4, two bumps 122 are separated by a predetermined distance, that determine the bump pitch 408 in combination with the overall width of the bump 122 and related structures making up a single BoT interconnect. In some embodiments, an adjacent trace 414 may be disposed near a BoT interconnect, and separated from a bump 122 by a bump-to-trace separation width 418. In some embodiments, the adjacent trace width 412 may be narrower than trace width 314. However, the adjacent trace is not limited to having a narrower width, as any dimension of adjacent trace 414 may be used.

The bump pitch 408 is the distance between like elements on adjacent structures, and is comprised of the bump separation distance 402 and the bump width 410, and in one embodiment, the bump pitch 408 may be about 140 μm or less. For the bumps 122 illustrated here, the minimum bump pitch 408 may be determined at least partly by the bump width 410, but also by the solder joint separation width 404 and bump-to-trace separation width 418. The trace separation distance 406 is determined by the bump separation distance 402 in combination with the difference between the trace width 314 and the bump width 410. The solder joint separation width 404 will, in one embodiment, be greater than the bump width 410. This results in a conductive material joint having a width less than the bump width 410.

The solder joint separation width 404 will, in one embodiment, be greater than the bump width 410. In an embodiment with a bump 122 having tapered sidewalls, the solder joint 124 may have a width less than the width of the widest part of the bump 122, or the bump width 410 illustrated herein, and may simultaneously have a width greater than the bump face width 312. Additionally, the solder joint 124 may have a width less than the bump width 410.

The width of the solder joint 124 may be determined by the volume of solder applied to form the solder joint 124. In one embodiment, the volume of solder required to form a solder joint 124 having a predetermined width and trace sidewall wetted region height 304 may be determined by the joint gap distance 308, solder joint separation width 404, bump-to-trace separation distance 416, trace 116 geometry, adjacent trace 414 geometry, and bump 122 geometry. In one embodiment, the volume of solder forming the solder joint 124 will be sufficient to wet the trace 116 sidewalls to a desired height and still provide a solder joint separation width 404 sufficient to prevent bridging of a solder joint 124 to an adjacent solder joint 124 or connection structure.

A method for forming a wetted sidewall trace BoT joint may, in one embodiment, comprise providing a first substrate 102 or other substrate, and forming one or more bumps 122 on the first substrate 102. The volume of a conductive material, such as solder, required for a predetermined width of solder joint 124 may optionally be calculated or optimized using joint parameters including, but not limited to one or more of the joint gap distance 308, a predetermined or desired solder joint width, a predetermined solder joint separation 404, the bump 122 geometry, the trace 116 geometry, the minimum trace 116 sidewall wetting region height or trace separation distance 406. The solder joint 124 may be applied in the calculated volume to the bump 122 as a solder cap.

The first substrate 102 may be singulated or removed from a wafer, singly or in predetermined first substrate 102 strips or groups, and may have final packaging steps performed. A second substrate 120, such as a PCB, chip, package, die, or the like, may be created by placing one or more traces 116 on a die substrate 114, and the first substrate 102 may then be placed on the second substrate 120, with the bump 122 and applied solder caps aligning with traces 116 on the second substrate 120. The assembly of the first substrate 102 and second substrate 120 may be heated for reflow to a temperature where, preferably, the solder reaches at least a eutectic point such that the solder melts or solidifies in a single step, without intermediate phases. The first substrate 102 may be moved towards or held apart from the second substrate 120 at a predetermined distance during reflow so that the bump faces 310 are about a predetermined joint gap distance 308 above the faces of the traces 116, and so that the solder of the solder bump wets the sidewall of the trace 116 to cover about a predetermined portion of the trace 116 sidewall.

FIG. 5A illustrates another embodiment of a BoT joint. In such an embodiment, the solder joint 124 may wet the sidewalls of the trace 116, while not wetting the sidewalls of the bump 122. Alternatively, as illustrated in FIG. 5C, the solder ball may wet one side of the bump 122, and not the other. This may be the result of the solder joint 124 forming a bulge where the solder fails to flow along the bump 122 sidewall. This may also be a result of the trace 116 being offset from the bump 122. Thus, the BoT may correct for accidental or intentional misalignment of the trace 116 and bump 122, permitting packages with mismatched mounting arrangements to be joined.

FIG. 5B illustrates an embodiment of a BoT joint with an alternative bump. In such an embodiment, the bump face width 312 may be greater than the base of the bump 122 having bump width 410. The solder joint 124 may, in such an embodiment, wet the sidewalls of the bump 122, further strengthening the attachment of the solder joint 124 to the bump 122 by mechanical means.

Although the present disclosure and its advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the disclosure as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, and composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure that processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. 

What is claimed is:
 1. A semiconductor device comprising: a first substrate; a bump disposed on the first substrate; a second substrate; a conductive trace disposed on the second substrate and having a sidewall; and solder electrically connecting the bump and the conductive trace, wherein the solder covers at least half the height of the sidewall of the conductive trace; wherein the bump is separated from the conductive trace by a distance less than the height of the sidewall of the conductive trace.
 2. The device of claim 1 wherein the bump is a copper bump.
 3. The device of claim 1 wherein the bump has substantially vertical sidewalls.
 4. The device of claim 1 wherein the bump has sloped sidewalls.
 5. The device of claim 4 wherein the solder covers at least a portion of a sidewall of the bump.
 6. The device of claim 1 wherein the solder covers the entirety of the sidewall of the conductive trace.
 7. The device of claim 1 wherein the bump is separated from the conductive trace, and wherein the solder is disposed between the bump and the conductive trace.
 8. A device comprising: a first bump; a first conductive trace having a sidewall; and a conductive material joint electrically connecting the first bump and the first conductive trace, wherein the conductive material covers at least half the height of the sidewall of the conductive trace; wherein the first bump is separated from the first conductive trace by a distance less than the height of the sidewall of the first conductive trace.
 9. The device of claim 8 wherein the first bump has sloped sidewalls.
 10. The device of claim 8, further comprising a first substrate having a conductive land, the first bump disposed on the conductive land.
 11. The device of claim 10, further comprising a passivation layer disposed on the first substrate and at least partially covering the land and defining an opening over the land, the first bump covering at least a portion of the passivation layer.
 12. The device of claim 10 wherein the conductive material is solder.
 13. The device of claim 11 wherein the joint is narrower than the first bump.
 14. The device of claim 10, further comprising a second bump, the first bump and second bump having a bump pitch of less than about 100 μm.
 15. A method comprising: providing a first substrate having a bump disposed thereon, and the bump having a volume of conductive material disposed thereon; providing a second substrate having a conductive trace, the conductive trace having a sidewall; and mounting the first substrate on the second substrate, the mounting resulting in an electrical connection from the bump to the conductive trace; wherein the bump is separated from the trace by a distance less than the height of the trace; and wherein the conductive material covers at least half the sidewall of the conductive trace.
 16. The method of claim 15 wherein: providing a first substrate comprises forming a plurality of bumps on the first substrate, each of the plurality of bumps having a volume of conductive material disposed thereon; providing a second substrate comprises forming a plurality of conductive traces on the second substrate; and mounting the first substrate to the second substrate comprises electrically connecting the plurality of bumps with respective ones of the plurality of conductive traces.
 17. The method of claim 16, wherein the conductive material is solder.
 18. The method of claim 17, further comprising calculating a volume of solder to form a solder joint having a predetermined width.
 19. The method of claim 18, wherein the volume of solder to form a solder joint having a predetermined width is calculated based on at least one of a joint gap distance, a desired solder joint width, a predetermined solder joint separation, a bump geometry, a trace geometry, a minimum trace sidewall wetting region height and a trace separation distance.
 20. The method of claim 18, wherein the predetermined width is less than the width of the bump. 